Mechanochemical Synthesis and DC Electrical Conductivity of PANI-Based MWCNT Containing Nanocomposites with Te 0 and Bi 2 Te 3 Thermoelectric Nanophase. |
| المؤلفون: |
Zhmurova, Anna V., Prozorova, Galina F., Zvereva, Marina V. |
| المصدر: |
Powders; Sep2023, Vol. 2 Issue 3, p540-561, 22p |
| مصطلحات موضوعية: |
MULTIWALLED carbon nanotubes, NANOCOMPOSITE materials, ELECTRIC conductivity, X-ray diffractometers, NANOSTRUCTURED materials |
| مستخلص: |
Nowadays, the search for the coupled polymer nanocomposite thermoelectrics that exhibit a high value of thermoelectric figure of merit (ZT) and similar behaviour of physical properties for the use as legs of thermoelectric cells is a current challenge. The direct current (DC) conductivity is one of the three important components of thermoelectric figure of merit. The aim of this study was to obtain PANI-based nanothermoelectrics with Te0 and Bi2Te3 nanoparticles and MWCNT by mechanochemical methodology and to investigate the dependency of their DC electrical conductivity on temperature in the 298–353 K range using the Arrhenius and Mott's variable range hopping (VRH) models. Inorganic Te0 and Bi2Te3 nanoparticles were pre-synthesized by the available and environmentally friendly method using a commercial tellurium powder. The samples obtained were characterized by X-ray diffractometry (XRD), IR and UV-Vis spectroscopy. The XRD study of ES-PANI/Te0 (4.4 wt% Te0) and ES-PANI/Bi2Te3 (2.9 wt% Bi2Te3) nanocomposites found that the nanoparticle average size was 32 nm and 17 nm, respectively. The DC conductivity study of the samples with different nanophase content (2.1, 4.4, 10.2 wt% Te0, 1.5, 2.9, 7.3 wt% Bi2Te3, 1.5 wt% MWCNT) by the two points measurement method reveals the following: (a) the presence of inorganic nanophase reduces the conductivity compared to the matrix, (b) the addition of MWCNT in ES-PANI increases its electrical conductivity, (c) the conductivity of ES-PANI/Te0 as well as ES-PANI/Bi2Te3 nanocomposite rises with the increasing inorganic nanophase content, (d) the observed increase in the electrical conductivity of MWCNT-based nanocomposites with increasing inorganic nanophase content is interrupted by a characteristic area of decrease in its value at average values of inorganic nanoparticles content (at Te0 content of 4.4 wt%, at Bi2Te3 content of 2.9 wt%), (e) a similar DC conductivity behaviour in ES-PANI/Te0—ES-PANI/Bi2Te3 and ES-PANI/Te0-MWCNT—ES-PANI/Bi2Te3-MWCNT nanocomposite pairs is observed. [ABSTRACT FROM AUTHOR] |
|
Copyright of Powders is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder