Residual stresses in Cu matrix composite surface deposits after laser melt injection. |
المؤلفون: |
Zhang, Xingxing, Kornmeier, Joana R., Hofmann, Michael, Langebeck, Anika, Alameddin, Shadi, Alessio, Renan Pereira, Fritzen, Felix, Bunn, Jeffrey R., Cabeza, Sandra |
المصدر: |
Strain; Dec2023, Vol. 59 Issue 6, p1-11, 11p |
مصطلحات موضوعية: |
RESIDUAL stresses, COPPER, METALLIC composites, FINITE element method, MATRIX-assisted laser desorption-ionization, TUNGSTEN carbide, LASER peening, NEUTRON diffraction |
مستخلص: |
Tungsten carbide particles reinforced metal matrix composite (MMC) coatings can significantly improve surface wear resistance owing to their increased surface hardness. However, the presence of macro‐ and micro‐residual stresses in MMC coatings can have detrimental effects, such as reducing service life. In this study, neutron diffraction was used to determine the residual stresses in spherical fused tungsten carbide (sFTC) reinforced Cu matrix composite surface deposits after laser melt injection. We also developed a thermo‐mechanical coupled finite element model to predict residual stresses. Our findings reveal that sFTC/Cu composite deposits produced with a preheating temperature of 400°C have low residual stresses, with a maximum tensile residual stress of 98 MPa in the Cu matrix on the top surface. In contrast, the sFTC/bronze (CuAl10Ni5Fe4) composite deposit exhibits very high residual stresses, with a maximum tensile residual stress in the Cu matrix on the top surface reaching 651 MPa. These results provide a better understanding of the magnitudes and distributions of residual stresses in sFTC‐reinforced Cu matrix composite surface deposits manufactured via laser melt injection. [ABSTRACT FROM AUTHOR] |
|
Copyright of Strain is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |