Influence of H on Sn incorporation in GeSnC alloys grown using molecular beam epitaxy. |
| المؤلفون: |
Dey, Tuhin, Arbogast, Augustus W., Meng, Qian, Reza, Md. Shamim, Muhowski, Aaron J., Cooper, Joshua J. P., Ozdemir, Erdem, Naab, Fabian U., Borrely, Thales, Anderson, Jonathan, Goldman, Rachel S., Wasserman, Daniel, Bank, Seth R., Holtz, Mark W., Piner, Edwin L., Wistey, Mark A. |
| المصدر: |
Journal of Applied Physics; 11/21/2023, Vol. 134 Issue 19, p1-12, 12p |
| مصطلحات موضوعية: |
MOLECULAR beam epitaxy, SCANNING transmission electron microscopy, TIN, X-ray photoelectron spectroscopy, RAMAN spectroscopy, ATOMIC hydrogen, SEMICONDUCTOR lasers, FULLERENES |
| مستخلص: |
GeSnC alloys offer a route to direct bandgap semiconductors for CMOS-compatible lasers, but the use of CBr4 as a carbon source was shown to reduce Sn incorporation by 83%–92%. We report on the role of thermally cracked H in increasing Sn incorporation by 6x–9.5x, restoring up to 71% of the lost Sn, and attribute this increase to removal of Br from the growth surface as HBr prior to formation of volatile groups such as SnBr4. Furthermore, as the H flux is increased, Rutherford backscattering spectroscopy reveals a monotonic increase in both Sn and carbon incorporation. X-ray diffraction reveals tensile-strained films that are pseudomorphic with the substrate. Raman spectroscopy suggests substitutional C incorporation; both x-ray photoelectron spectroscopy and Raman suggest a lack of graphitic carbon or its other phases. For the lowest growth temperatures, scanning transmission electron microscopy reveals nanovoids that may account for the low Sn substitutional fraction in those layers. Conversely, the sample grown at high temperatures displayed abrupt interfaces, notably devoid of any voids, tin, or carbon-rich clusters. Finally, the surface roughness decreases with increasing growth temperature. These results show that atomic hydrogen provides a highly promising route to increase both Sn and C to achieve a strongly direct bandgap for optical gain and active silicon photonics. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |