التفاصيل البيبلوغرافية
| العنوان: |
FRACTURE-BEHAVIOR OF CAD/CAM CERAMIC CROWNS BEFORE AND AFTER CYCLIC FATIGUE AGING. |
| المؤلفون: |
Garoushi, Sufyan, Säilynoja, Eija, Vallittu, Pekka K., Lassila, Lippo |
| المصدر: |
International Journal of Prosthodontics; Sep/Oct2023, Vol. 36 Issue 5, pe29-e37, 9p, 2 Charts |
| مصطلحات موضوعية: |
DENTAL crowns, CYCLIC fatigue, LITHIUM silicates, CERAMIC materials, TWO-way analysis of variance |
| الشركة/الكيان: |
AKER ASA |
| مستخلص: |
Purpose: To evaluate the fracture-behavior of monolithic crowns made of lithium disilicate (IPS e.max CAD, Ivoclar Vivadent; IniBal LiSi Block, GC Dental) and zirconia-reinforced lithium silicate (Celtra Duo, DeguDent; VITA Zahnfabrik) materials before and aKer cyclic faBgue aging. Materials and Methods: Four groups (n = 22/group) of CAD/CAM fabricated upper incisor crowns were produced. All crowns were luted on metal dies with an adhesive dualcure resin cement (G-CEM LinkForce, GC Dental). Half of the crowns in each group (n = 11) were staBcally loaded unBl fracture, without aging. The remaining crowns were subjected to cyclic faBgue aging for 120,000 cycles (Fmax = 220 N) and then loaded staBcally unBl fracture. The fractured models were then visually examined. Scanning electron microsopy (SEM) and energy-dispersive spectroscopy (EDS) were used to evaluate the microstructure of CAD/CAM ceramic materials. The data were staBsBcally analyzed with two-way ANOVA followed by the Tukey HSD test (a = .05). Results: Before cyclic aging, there was no staBsBcally significant difference in load-bearing capacity among the four groups (P = .371). AKer cyclic aging, load-bearing capacity significantly decreased for all groups (P = .000). While the e.max CAD blocks had significantly higher load-bearing capacity (1061 ± 94 N) than both monolithic ceramic crowns (load-bearing capaciBes of the groups) (P < .05), no significant difference was obtained with the IniBal LiSi Block group (920 ± 140 N) (P = .061). Conclusions: The mechanical performance of monolithic ceramic crowns fabricated from lithium disilicate was befer than zirconia-reinforced lithium silicate aKer cyclic faBgue aging. [ABSTRACT FROM AUTHOR] |
|
Copyright of International Journal of Prosthodontics is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |