Effect of Deposition Temperature on Microstructure and Friction/Wear Properties of C/C Composites Prepared by CVI+PIP Process. (English) |
المؤلفون: |
MA Yuqin, WANG Yinghao, LI Fei, JU Luyan, WANG Gangfeng, WANG Hao |
المصدر: |
Journal of Materials Science & Engineering (1673-2812); Oct2023, Vol. 41 Issue 5, p775-785, 11p |
مستخلص: |
A combination of chemical vapor infiltration (CVI) and polymer impregnation pyrolysis (PIP) was used to prepare carbon/carbon (C/C) composites. CFT-I comprehensive material surface property tester was used to perform reciprocal friction wear test on the C/C composite. Scanning electron microscope was used to characterize the microstructure and post-friction surface morphology of C/C composites. The effect of deposition temperature on the microstructure and friction/wear properties of C/C composites prepared by CVI +PIP processes was investigated. The results show that C/C composites present more desirable friction wear performance compared with graphite materials. The C/C composite with very few holes and cracks at the deposition temperature of 1 050 °C show a stable friction coefficient and the lowest wear rate, and the frictional wear performance is ideal. The infiltration effect is the best. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Science & Engineering (1673-2812) is the property of Journal of Materials Science & Engineering Editorial Office and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |