Failure Assessment and High-Temperature Corrosion Behavior of Inconel 625 Welds in Simulated K2SO4 + 60% NaCl Boiler Environment. |
المؤلفون: |
Prabu, S. Senthur, Muthu, S. M., Sujai, S., Ramkumar, K. Devendranath, Beemkumar, N., Kariappan, Elangovan |
المصدر: |
Journal of Materials Engineering & Performance; Dec2023, Vol. 32 Issue 24, p11024-11039, 16p |
مصطلحات موضوعية: |
FUSION zone (Welding), GAS tungsten arc welding, WELDED joints, INCONEL, FUSED salts |
مستخلص: |
This research investigates the hot corrosion behavior of Inconel 625 similar joints welded using pulsed current gas tungsten arc welding (PCGTAW). Specific emphasis has been given to the microstructural changes at the fusion zone and weld interface while employing two different Ni-Mo-rich fillers (ERNiCrCoMo-1 and ERNiCrMo-4). The microstructure of the weldments was evaluated using scanning electron microscopy (SEM) and optical microscopy (OM) techniques. The weld joints employed with ERNiCrMo-4 filler showed slightly higher strength than that of ERNiCrCoMo-1, and the fractures were found on the base metal regions. The performance of the alloy 625 bi-metallic joints has been ascertained by exposing both cyclic molten salt K2SO4 + 60% NaCl and an air oxidation environment at 700 °C. A thermogravimetric plot was employed to determine the weldment kinetics of corrosion. SEM/EDS systematically examined the oxide scales formed on the weldments, and x-ray diffraction (XRD) was used to identify the phases of the corrosion products. The test results revealed that the corroded samples in the salt condition experienced severe corrosion attacks as compared to air conditions by sulfidation and chlorination. Based on the specific outcomes of this study, ERNiCrMo-4 filler is recommended for joining these similar combinations of welds and it imparts better corrosion resistance at elevated temperatures in simulated boiler environments. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Engineering & Performance is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |