Effects of Chitosan on the Characteristics of Sorbitol Plasticised Cellulose Acetate/Starch Bioplastics. |
| المؤلفون: |
Rahmatullah, Putri, Rizka Wulandari, Nurisman, Enggal, Susmanto, Prahady, Haryati, Sri, Waristian, Harry, Zulkifli, Muzafar, Minata, Tree Silvia Putri, Meidina, Shenia |
| المصدر: |
CET Journal - Chemical Engineering Transactions; 2023, Vol. 106, p259-264, 6p |
| مصطلحات موضوعية: |
CHITOSAN, CELLULOSE acetate, BIODEGRADABLE plastics, PLANT fibers, ELASTICITY |
| مستخلص: |
Due to the natural origins of its primary components, such as plant fibers, bioplastics are materials that disintegrate quickly. Typically, plasticizers are used to create cellulose-based bioplastics. Plasticizers soften hard, inflexible structures, improve elasticity and flexibility, and lessen bioplastics' tendency to break. The manufacturing of bioplastics in this study includes the incorporation of chitosan and sorbitol plasticizers as a variable. Chitosan and sorbitol were utilized in the following mass ratios: 0.5 g, 1.0 g, and 20 %, 30 %, and 40 %. The optimal chitosan and sorbitol concentrations produced the most desirable bioplastic properties. At a ratio of 20 % sorbitol and 0.5 g chitosan, the greatest bioplastic value for tensile strength (845.68 kPa) and Young's modulus (67.65 x 102 KPa) was attained. With values of 44.94 % and 81.28 %, respectively, the ratio of 30 % sorbitol to 1 g chitosan produced the best mass and water absorption values. At a ratio of 30 % sorbitol and 0.5 g chitosan at 0.94 g/mL and a ratio of 40 % sorbitol and 1 g chitosan at 1.75 %, the highest density and elongation values were identified. [ABSTRACT FROM AUTHOR] |
|
Copyright of CET Journal - Chemical Engineering Transactions is the property of AIDIC Servizi Srl, Italian Association of Chemical Engineering and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder