| العنوان: |
Self-Tunable, Exfoliated Oxygen-Rich Flower-like MoS2 Nanosheets for Arsenic Removal: Investigations on Substitution, Stability, and Sustainability (3S) for Maxi-Sorption. |
| المؤلفون: |
Muthu Prabhu, Subbaiah, Rubini, Kamatchi, Pyo, Seong-Hyeon, Pandi, Kalimuthu, Krishna Kumar, A. Santhana, Mandlimath, Triveni Rajashekar, Cheon, Ji-Kwang, Jung, Jinho, Yadav, Krishna Kumar, Park, Ho Bum, Jeon, Byong-Hun |
| المصدر: |
ACS Applied Nano Materials; 1/26/2024, Vol. 7 Issue 2, p1907-1918, 12p |
| مستخلص: |
In this study, we synthesized La-incorporated O-rich defective MoS2 nanosheets by a simple, inexpensive, in situ hydrothermal reaction to self-exfoliate the bulky MoS2 layers themselves so that they can readily trap hard base anions, arsenic (arsenite and arsenate), from water. Attempting to modify MoS2 surfaces by incorporating O allows for more active sites, which is confirmed by powder XRD patterns where the exfoliated layers have a d-spacing of 0.63 nm, while the spacing for the bulky layers is 0.60 nm. The substitution of La at different equivalent ratios on the interlayer/surface improves the adsorption properties of arsenite and arsenate in simple solutions, as shown by the Langmuir adsorption density values of 0.7760 and 1.4363 mmol g–1, respectively. When the O-rich MoS2 layers were loaded with La, the adsorption densities improved, with La1.0 equiv showing the best values among the materials studied. The presence of O and S was more responsible for the removal of arsenite ions, and La and O, together with a small amount of N, were able to remove arsenate ions from water according to the well-known Pearson's Lewis acid−base principle. The stability of the materials was characterized after the experiments, and it was found that there was no leaching of the materials by ICP-OES and the stability was maintained after 6 regeneration cycles. With the exception of phosphate, which behaves chemically similar to arsenic, the adsorption densities were not significantly affected by the mono- and divalent anions, indicating the selectivity of the prepared materials. The synthesis cost of MoOxS2–x was 2 times lower than that of bulky MoS2, and its adsorption properties were 10 times higher than those of the latter. The results suggest that La-substituted O-rich MoS2 is a potential candidate for the removal of soft and hard base metals from water. [ABSTRACT FROM AUTHOR] |
|
Copyright of ACS Applied Nano Materials is the property of American Chemical Society and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |