التفاصيل البيبلوغرافية
| العنوان: |
Carrier transport in LPCVD grown Ge-doped β-Ga2O3/4H-SiC isotype heterojunction. |
| المؤلفون: |
Saquib, T., Akyol, F., Ozden, H., Somaiah, N., Sahoo, J., Muralidharan, R., Nath, D. N. |
| المصدر: |
Journal of Applied Physics; 2/14/2024, Vol. 135 Issue 6, p1-8, 8p |
| مصطلحات موضوعية: |
TWO-dimensional electron gas, HETEROJUNCTIONS, SCHOTTKY barrier, CHEMICAL vapor deposition, ELECTRON transport, RADARSAT satellites |
| مستخلص: |
We report on the study of electron transport and band offset across β -Ga 2 O 3 /4H-SiC N–n isotype heterojunction. N-type β -Ga 2 O 3 of thickness 2.7 μ m was grown using low-pressure chemical vapor deposition using germanium (Ge) as the dopant on an n-type 4H-SiC substrate. The grown epilayer having (− 201) orientation was verified through XRD. Temperature-dependent I–V and C–V measurements were performed (50–300 K) to investigate the transport properties across the heterojunction. First, lateral diodes were fabricated on β -Ga 2 O 3 , and from C–V, n-doping was estimated to be 2.3 × 10 17 cm − 3 in the epilayer while the Schottky barrier height was estimated to be 1.75 eV. In top-down I–V sweeps, the reverse current across the heterojunction exhibited marginal dependence on temperature, indicating a possible tunnelling-based transport mechanism, while the forward current exhibited an exponential dependence on both temperature and the applied bias. The band diagram indicated the formation of a two-dimensional electron gas (2DEG) at the hetero-interface, which was indirectly confirmed using C–V measurement and TCAD simulation at low temperatures. From the position of the Fermi level in SiC and band diagram, a conduction band offset of 0.4–0.5 eV was estimated between β -Ga 2 O 3 and 4H-SiC. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |