Sustain the properties of dissimilar joints by alternative filler alloy. |
| المؤلفون: |
Jawad, Sarah M., AL-Roubaiy, Ahmed O., Al-Shafaie, Saad H. |
| المصدر: |
AIP Conference Proceedings; 2024, Vol. 3092 Issue 1, p1-6, 6p |
| مصطلحات موضوعية: |
FILLER metal, MICROHARDNESS testing, SHEAR strength, JOINING processes, X-ray diffraction, ALLOYS, COPPER-titanium alloys |
| مستخلص: |
Ti6Al4V/ZrO2 joints prepared by brazing process with two types Ag-Cu- Ti alloy as a metal filler. The joining process done under inert atmosphere (argon) in different temperature's (850,875, 900 and 925 ℃) for 20 minutes. The mechanical properties tested by singe shear test and microhardness test with using SEM, EDS and XRD to investigate the fractured surfaces after shear test. The results show, raising temperature increasing the shear strength until 875℃ then gradually decrease for both filler types. The maximum shear strengths for prepared joints with filler 2 are slightly higher than that for joints with filler 1. The micro hardness of both types of joints increased as temperature increased. [ABSTRACT FROM AUTHOR] |
|
Copyright of AIP Conference Proceedings is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Scitation.