التفاصيل البيبلوغرافية
| العنوان: |
Microstructure and Properties of Hot Pressing Sintered SiC/Y 3 Al 5 O 12 Composite Ceramics for Dry Gas Seals. |
| المؤلفون: |
Zou, Chang, Ou, Yangxin, Zhou, Weiliang, Li, Zhiqiang, Zheng, Pu, Guo, Xingzhong |
| المصدر: |
Materials (1996-1944); Mar2024, Vol. 17 Issue 5, p1182, 12p |
| مصطلحات موضوعية: |
YTTRIUM aluminum garnet, HOT pressing, MICROSTRUCTURE, CERAMICS, SPECIFIC gravity, CENTRIFUGAL compressors |
| مستخلص: |
Silicon carbide (SiC) ceramics with high bending strength were prepared by hot pressing sintering (HPS) with yttrium aluminum garnet (Y3Al5O12, YAG) as sintering additive, and the effects of YAG content and sintering temperature on the sintering behavior, microstructure and mechanical properties of SiC ceramics were investigated in detail. The uniform distribution of YAG to form a liquid phase and the driving force provided by hot pressing sintering decrease the sintering temperature, improve the densification of SiC ceramics, and refine the crystal size. By means of suitable sintering conditions with the additional amount of YAG of 5 wt%, the sintering temperature of 1950 °C and a pressure of 30 MPa, the resultant SiC/YAG composite ceramics possesses high sintering and mechanical properties with the relative density of 98.53%, the bending strength of 675 MPa, the Vickers hardness of up to 17.92 GPa, and the elastic modulus of 386 GPa. The as-prepared SiC/YAG composite ceramics are promisingly used as the dry gas seal materials in the centrifugal compressors. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |