| العنوان: |
Continuous strain-mediated perpendicular magnetic anisotropy in epitaxial (111) CoFe2O4 thin films grown on LiTaO3 substrates. |
| المؤلفون: |
Wang, S., Hu, L., Zhang, G. D., Wei, R. H., Song, W. H., Zhu, X. B., Sun, Y. P. |
| المصدر: |
Journal of Applied Physics; 3/28/2024, Vol. 135 Issue 12, p1-7, 7p |
| مصطلحات موضوعية: |
MAGNETIC anisotropy, PERPENDICULAR magnetic anisotropy, THIN films, MAGNETIC films, MAGNETOELASTIC effects, CHIEF financial officers, THERMAL expansion |
| مستخلص: |
Perpendicular magnetic anisotropy (PMA) in magnetic thin films has attracted much attention due to its potential applications in spintronics devices. Here, we report the continuous strain-mediated PMA in epitaxial (111) CoFe 2 O 4 (CFO) thin films grown on (0001) LiTaO 3 substrates. A large variation in lattice strain (∼ 0.9 %) in a continuous way is realized in the CFO thin films by changing substrate temperature during deposition due to the difference in the thermal expansion coefficient between CFO and LiTaO 3. As a result, the PMA of the (111) CFO thin films can be continuously mediated by the strain with uniaxial magnetic anisotropy energy in the range of 0.12 - 14.69 × 10 6 erg/cm 3. Furthermore, the strain as well as the consequent PMA in the (111) CFO thin films can be maintained within the thickness of 25–205 nm, which is consistent with the scenario of the magnetoelastic effect. Our results reveal that the CFO/LiTaO 3 system can be regarded as an ideal platform to realize robust PMA and its continuous strain tuning in the (111) CFO thin films by virtue of strain-induced magnetic anisotropy. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |