Effect of Silicon Addition on Microstructure, Hardness and Young's Modulus of Injection Molded AZ91D Alloy. |
| المؤلفون: |
Yasutoshi Hideshima, Fumiya Maeda, Tadao Fukuta, Koichi Ozaki |
| المصدر: |
Materials Transactions; 2024, Vol. 65 Issue 4, p368-373, 6p |
| مصطلحات موضوعية: |
YOUNG'S modulus, HARDNESS, MICROSTRUCTURE, SILICON, ALLOYS |
| مستخلص: |
Magnesium chips were coated with silicon powder using a binder, and injection molding was performed using silicon-coated chips as the raw material. Microstructural analysis of the products revealed that all added silicon (Si) precipitated as Mg2Si particles, with no voids present at the interfaces between the Mg2Si particles and the matrix. Furthermore, the hardness and Young's modulus of the products increased with higher Si content. The Young's moduli followed the rules of mixtures. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials Transactions is the property of Japan Institute of Metals & Materials and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |