Enhanced structural properties of electrochemically synthesised NiFeS using 500 keV carbon C++ ions irradiation. |
| المؤلفون: |
Okeoghene Blessing, Ijabor, Shah, Haneef, Afzal, Shahbaz, Ikhioya, Imosobomeh L. |
| المصدر: |
Materials Research Innovations; Jun2024, Vol. 28 Issue 4, p251-262, 12p |
| مصطلحات موضوعية: |
IRON sulfides, IRON-nickel alloys, CARRIER density, OPTOELECTRONIC devices, SOLAR cells, ELECTRIC conductivity, IRRADIATION |
| مستخلص: |
An electrochemical approach was used to synthesise nickel iron sulphide (NiFeS) materials in this work. The prepared NiFeS underwent a thorough investigation, which included analyses of its optical, electrical, structural, morphological, elemental, and functional group properties. Cubic crystal formations with prominent peaks were visible from the structural pattern. Nanoflakes and pebbles were visible, and their elements were determined through elemental dispersive X-ray diffractometer (EDX) spectrum. The film's crystallinity increased after incorporating carbon ions and its optical properties improved, with energy band gap values ranging from 1.50 eV to 1.15 eV as the peaks became more distinct. The materials produced could be utilised in the production of solar cells and optoelectronic devices. The electrical conductivity diminishes with increasing thickness. Carbon ion radiation increases carrier concentration, which increases electrical conductivity. NiFeS was irradiated using 500 keV carbon C++ ions beam irradiation NiFeS without irradiation has a bandgap of 1.50 eV, while the irradiated material had bandgaps between 1.35-1.15 eV. The film's crystallinity was enhanced by incorporating carbon ions Nanogels and nanoflakes were seen in the micrographs of the unirradiated materials. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials Research Innovations is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |