锑电积贫液中锑回收试验研究. (Chinese) |
Alternate Title: |
Experimental study on antimony recovery from antimony electrolytic deposition lean solution. (English) |
المؤلفون: |
赵娜, 臧文优, 栾东武, 孙美芬, 王杰 |
المصدر: |
Gold (1001-1277); May2024, Vol. 45 Issue 5, p50-79, 5p |
Abstract (English): |
In response to the high content of antimony in the lean solution of antimony electrolytic deposition and the high grade of antimony in the agitation rate antimony residue from acidification and precipitation, which leads to low antimony recovery in alkaline leaching after blending with low-grade ore, experiments were conducted on acidification and precipitation of antimony cooling crystallization alkaline leaching electrolytic deposition process. Through single-factor acidification and precipitation experiments, the effects of pH, reaction temperature, agitation rate, and cooling crystallization on the effect of acidification and precipitation of antimony were investigated. The results show that under the conditions of pH 5 for acidification and precipitation of antimony, a cooling crystallization temperature of 10°C a slurry concentration of 20% for alkaline leaching, Na2S concentration of 85 g/L, NaOH concentration of 40 g/L, alkaline leaching time of 1 h, NaOH concentration of 70 g/L in the electrolytic deposition solution, current of 4. 80 A, cathode area to anode area ratio of 5.8:1, and electrolytic deposition time of 50 h, the antimony recovery rate in the electrolytic deposition experiment reached 82.29%, with an antimony grade on the cathode of 92.72%, thus enhanc- ing resource utilization. [ABSTRACT FROM AUTHOR] |
Abstract (Chinese): |
针对甘肃某公司锑电积贫液含锑较高,酸化沉锑渣锑品位高导致其与低品位矿配矿后 碱浸锑回收率低的问题,开展了酸化沉锑——冷却结晶———碱浸———电积试验研究。通过单因素试验 考察了pH、反应温度、搅拌速度和冷却结晶等对酸化沉锑效果的影响,结果表明:在酸化沉锑 pH=5,冷却结晶温度10℃,碱浸矿浆浓度20%、Na₂S质量浓度85g/L、NaOH质量浓度40g/L、 碱浸时间1h、电积NaOH质量浓度70g/L、电流4.80A、阴极与阳极面积比为5.8:1、电积时 间50h的条件下,电积试验锑回收率为82.29%,阴极锑品位为92.72%,提高了资源利用 率。 [ABSTRACT FROM AUTHOR] |
|
Copyright of Gold (1001-1277) is the property of Gold Magazine Editorial Office and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |