Study on the interfacial microstructure evolution of aluminum and CFRTP on FSLW joints: influence of pin length. |
| المؤلفون: |
Sun, Yibo, Zhang, Yuan, Long, Haiwei, Zhu, Jianning, Fu, Libin, Yang, Xinhua |
| المصدر: |
Journal of Adhesion Science & Technology; Jun2024, Vol. 38 Issue 12, p2209-2221, 13p |
| مصطلحات موضوعية: |
FRICTION stir welding, POLYETHYLENEIMINE, DISSIMILAR welding, MICROSTRUCTURE, ZONE melting, TENSILE tests, CARBON composites |
| مستخلص: |
Polymer/metal hybrid lightweight structures are increasingly employed in automotive, aerospace and electronics industries. Friction stir welding (FSW) is applied for the effective welding of metals and thermoplastic materials. For the welding of dissimilar materials, due to the significant property differences, it is hard to achieve high strength welded joints with smooth appearance. In this article, the influence of pin length is studied by experiments for the friction stir lap welding (FSLW) of Al alloy and carbon-fiber-reinforced thermoplastic (CFRTP). Tensile tests, OM, SEM and EBSD are carried out to evaluate the welding performance. Results indicate that the joint with smooth surface topography is obtained at the pin length of 2.5 mm with a peak temperature of 250.3 °C and the CFRTP matrix PEI thermal decomposition temperature residence time of 47.6 s. From OM and SEM micro analysis, the width of the bonding area is 3.02 mm and a thin uniform interaction layer is formed in the joint. EBSD confirms that the Al alloy in the stirring zone is refined after recrystallization. It is difficult to form a stacked layered structure in the bottom of joint, so the property of the joint is improved. The tensile strength is 32.9 MPa, which is 63.1% of CFRTP. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Adhesion Science & Technology is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |