Thermal Stability, Flame Retardancy and Flame Retardant Mechanisms of Hollow Glass Microspheres/Montmorillonite/Epoxy Sheet Molding Compound Composites. |
| المؤلفون: |
Huang, Zhixiong, Jiang, Guoqin, Li, Linxuan, Wu, Yue, Wu, Jialuo, Deng, Zongyi |
| المصدر: |
Journal of Macromolecular Science: Physics; 2024, Vol. 63 Issue 8, p621-633, 13p |
| مصطلحات موضوعية: |
FIREPROOFING, FIRE resistant polymers, FIREPROOFING agents, MONTMORILLONITE, HEAT release rates, EPOXY resins, THERMAL stability, SILANE coupling agents |
| مستخلص: |
Epoxy sheet molding compound (ESMC) composites have excellent mechanical properties, dimensional stability and electrical insulation, and are widely used in the automotive industry. In our previous work silane coupling agent modified, hollow glass microspheres (SiHGM) and montmorillonite (MMT) were incorporated to enhance the mechanical properties of the ESMC composites. It was found that the ESMC composites containing MMT (EP/SiHGM/MMT-1) exhibited excellent mechanical strength. However, the flammability of the epoxy resin (EP) limits the use of ESMC composites for applications that require good flame retardancy. In this paper we describe our research in which MMT was used to increase the flame retardancy of ESMC composites. The results showed that the addition of MMT made the ESMC composites have excellent flame retardancy. The limiting oxygen index (LOI) of the ESMC composites containing 1 phr MMT (EP/SiHGM/MMT-1) was 26.8%, which was 8.94% higher than that of the ESMC composites without MMT (EP/SiHGM/MMT-0). In addition, the peak heat release rate (PHRR), average heat release rate (AHRR) and total heat release (THR) of the EP/SiHGM/MMT-1 were 322.8 kW/m2, 95.3 kW/m2 and 38.6 MJ/m2, respectively, which were 22.6%, 8.2% and 8.0% lower than those of EP/SiHGM/MMT-0. The carbon monoxide production (COP) and carbon dioxide production (CO2P) of EP/SiHGM/MMT-1 were 0.0092 g/s and 0.2071 g/s, respectively, which were 34.3% and 22.8% lower than those of EP/SiHGM/MMT-0. The fire growth index (FGI) of EP/SiHGM/MMT-1 was 2.4, which was a decrease by 29.4% compared to EP/SiHGM/MMT-0. In addition, the flame retardant mechanisms were revealed. We suggest that MMT promoted dehydration and charring of the epoxy resin and helped construct an intact physical barrier, which had good blocking effects. The prepared composite has great application prospects for those occasions that require high flame retardancy. Thus, this work provides an innovative strategy for preparing low density epoxy composites with excellent flame retardancy and high mechanical properties. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Macromolecular Science: Physics is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |