Effects of Ti/Al Ratio on Formation of Ti-Al Intermetallics/TiB 2 Composites by SHS from Ti-Al-B Powder Mixtures. |
| المؤلفون: |
Yeh, Chun-Liang, Chan, Yi-Cheng |
| المصدر: |
Processes; Jun2024, Vol. 12 Issue 6, p1237, 12p |
| مصطلحات موضوعية: |
SELF-propagating high-temperature synthesis, POWDERS, MIXTURES, X-ray diffraction, INTERMETALLIC compounds, ACTIVATION energy, ALUMINUM composites, CARBON composites |
| مستخلص: |
Ti-Al intermetallics/TiB2 composites were prepared from elemental powder mixtures by the method of self-propagating high-temperature synthesis (SHS). Reactant mixtures were formulated to contain two parts; one group was (2Ti + 4B) to form 2TiB2 and the other group was (Ti + xAl) to produce Ti-Al intermetallic compounds. The content of Al ranged between x = 0.33 and 3.0, which was equivalent to the Ti/Al atomic ratio from Ti-25% Al to Ti-75% Al in the (Ti + xAl) group. The results showed that the increase of Al percentage reduced the overall combustion exothermicity and led to a slower self-sustaining combustion wave speed and a lower combustion temperature. Apparent activation energy of the Ti-Al-B solid-state combustion reaction was determined to be 114.7 kJ/mol by this study. Based on the XRD analysis, Ti-Al intermetallics/TiB2 composites featuring Ti3Al, TiAl, TiAl2, and TiAl3 as the dominant aluminide phase were respectively synthesized from the samples of Ti-25%~40% Al, Ti-50%~60% Al, Ti-71.4% Al, and Ti-75% Al. For the samples of Ti-25% Al and Ti-30% Al, Ti3Al was the only aluminide formed. The microstructure of the composites exhibited that TiB2 grains with a columnar shape of 2–3 μm in length were well distributed and embedded in the aluminide matrix. This study demonstrated an effective and energy-saving fabrication route for producing Ti-Al intermetallics/TiB2 composites with different dominant aluminide phases. [ABSTRACT FROM AUTHOR] |
|
Copyright of Processes is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder