HYDROGEN REDUCTION BEHAVIOR AND MICROSTRUCTURE CHARACTERISTICS OF WO3-NiO-CuO POWDER MIXTURE. |
| المؤلفون: |
YOUN JI HEO, EUI SEON LEE, JI YOUNG KIM, SUNG-TAG OH, JONGMIN BYUN |
| المصدر: |
Archives of Metallurgy & Materials; 2024, Vol. 69 Issue 2, p443-446, 4p |
| مصطلحات موضوعية: |
METAL powders, ALLOY powders, POWDERS, MICROSTRUCTURE, HYDROGEN, COPPER, MIXTURES |
| مستخلص: |
The characteristics and hydrogen reduction behavior of W-0.8 wt% Ni-0.4 wt% Cu powder synthesized from WO3-NiOCuO composite powder have been investigated. The metal oxide powder mixtures were prepared using a ball milling process. XRD analysis and HR-TEM revealed that the oxide powders are changed to W and CuNi alloy powders with an average particle size of about 100 nm by hydrogen reduction. To understand the reduction behavior of oxide powders, TG analysis was performed, and the reduction kinetics was evaluated by the amount of peak shift with heating rates. The activation energies for the reduction of WO3-NiO-CuO, estimated by the slope of the Kissinger plot, were measured as 60.6-114.4 kJ/mol depending on reduction steps. [ABSTRACT FROM AUTHOR] |
|
Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder