التفاصيل البيبلوغرافية
| العنوان: |
Numerical Simulation of Physical Field During Different Ultrasonic‐Power‐Assisted Casting of 7085 Aluminum Alloy. |
| المؤلفون: |
Li, Anqing, Jiang, Ripeng, Hai, Xiquan, Li, Ruiqing, Fu, Aolei, Li, Xiaoqian |
| المصدر: |
Advanced Engineering Materials; Jul2024, Vol. 26 Issue 13, p1-15, 15p |
| مصطلحات موضوعية: |
ALUMINUM castings, SOUND pressure, ALUMINUM alloys, COMPUTER simulation, ACOUSTIC field, ZONE melting |
| مستخلص: |
High‐energy ultrasound has the effect of purifying the aluminum (Al) melt and improving the uniformity of temperature and flow field distribution. In this article, a finite‐element numerical model of ultrasonic‐assisted casting of 7085 Al alloy melt is established, and the changes of acoustic pressure field, temperature field, and flow field in the solidification process of alloy melt with different ultrasonic power are investigated. In the numerical simulation results, it is shown that the thickness of the 7085 Al melt mushy zone decreases by 89, 97, 108, 114, and 99 mm, respectively, compared without ultrasonic (WNU) when the ultrasonic power is 150, 350, 550, 750, and 950 W. The area of the alloy mushy zone increases by 38.1%, 43.5%, 61.0%, 206.5%, and 45.6%, respectively. According to numerical simulation results, when the ultrasonic power is 750 W, it has the best effect on improving the macroscopic physical field, increasing the mass and heat‐transfer rate in the center of the Al melt. Meanwhile, the experimental results of industrial melting and casting of 7085 large‐scale Al alloy ingots are basically consistent with the numerical simulation, which provide technical support for ultrasonic‐assisted fabrication of large‐scale 7085 Al alloy ingots. [ABSTRACT FROM AUTHOR] |
|
Copyright of Advanced Engineering Materials is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |