Carbon Dioxide Capture Performance of Mesostructured Adsorbent Impregnated with Polyethylenimine. |
المؤلفون: |
Chien-Hung Chen, Ching-Tsung Yu, Yu-Fei Chang |
المصدر: |
International Journal of Engineering & Technology Innovation; Jul2024, Vol. 14 Issue 3, p298-308, 11p |
مصطلحات موضوعية: |
CARBON sequestration, POLYETHYLENEIMINE, MULTIWALLED carbon nanotubes, MESOPOROUS materials, DESORPTION kinetics, SORBENTS |
مستخلص: |
This study aims to investigate the CO2 uptake performance of mesostructured adsorbents, such as Mobil Composition of Matter No. 41 (MCM-41), Santa Barbara Amorphous-15 (SBA-15), and multi-walled carbon nanotubes (MWNTs), modified with polyethylenimine (PEI). Mesoporous materials are loaded with 50 wt.% PEI using a wet impregnation method. CO2 kinetic experiments of the PEI-modified adsorbents are conducted by a thermogravimetric method. The results reveal that the CO2 adsorption capacities of the PEI/MCM-41, PEI/SBA-15, and PEI/MWNTs composites are 2.02, 3.06, and 2.93 mmol/g, respectively, under 15% CO2 flow at 348 K. The lower CO2 adsorption capacity of PEI/MCM-41 (2.02 mmol/g) is attributed to its poor porosity. The PEI/MWNTs composite has the fastest CO2 adsorption and desorption kinetics at the same temperature, compared to other PEImodified adsorbents. These results suggest that MWNTs might play a significant "separator" role in effectively dispersing the PEI molecular chains on the mesostructured adsorbent. [ABSTRACT FROM AUTHOR] |
|
Copyright of International Journal of Engineering & Technology Innovation is the property of Taiwan Association of Engineering & Technology Innovation and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |