العنوان: |
Effect of Different Process Parameters on Three-Spot Laser Brazing of Galvanized Steel. |
المؤلفون: |
Li, Siliang, Liu, Haijiang, Zhang, Heng |
المصدر: |
Journal of Materials Engineering & Performance; Jun2024, Vol. 33 Issue 12, p5727-5734, 8p |
مصطلحات موضوعية: |
GALVANIZED steel, BRAZING, BRAZED joints, LASERS, SURFACE coatings, RIVETED joints, WELDING equipment |
مستخلص: |
Aiming at the problem of porosity in laser brazing of galvanized sheet, three-spot laser brazing technology was used to solve the problem of pores caused by evaporation of zinc vapor. The surface morphology and mechanical properties of galvanized sheet laser brazed joints with or without three spots were studied. The results showed that when the three-spot laser brazing technology was applied, the zinc coating on the surface of galvanized steel was removed by coating removal laser in advance, zinc vapor escaped completely, and there were no visible pores on the surface of the weld. For the tensile strength and microhardness of brazed joints, when the laser power was 2500-3200 W, the welding speed was 40-50 mm/s, the wire feeding speed was 3.0-3.5 m/min, and the beam-spot size was 4.2-5.5 mm; the tensile strength of the brazed joint reached more than 80% of the base metal. The tensile strength of the brazed joint was sensitive to welding speed. The microhardness of fusion zone was higher than base metal, and the microhardness reached 120 HV. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Engineering & Performance is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |