العنوان: |
Brittle Fracture Behavior of Sn-Ag-Cu Solder Joints with Ni-Less Surface Finish via Laser-Assisted Bonding. |
المؤلفون: |
Han, Seonghui, Han, Sang-Eun, Lee, Tae-Young, Han, Deok-Gon, Park, Young-Bae, Yoo, Sehoon |
المصدر: |
Materials (1996-1944); Jul2024, Vol. 17 Issue 14, p3619, 11p |
مصطلحات موضوعية: |
SOLDER joints, BRITTLE fractures, HIGH power lasers, INTERMETALLIC compounds, ELECTRONIC packaging |
مستخلص: |
In this study, we investigated the brittle fracture behavior of Sn-3.0Ag-0.5Cu (SAC305) solder joints with a Direct Electroless Gold (DEG) surface finish, formed using laser-assisted bonding (LAB) and mass reflow (MR) techniques. Commercial SAC305 solder balls were used to ensure consistency. LAB increases void fractions and coarsens the primary β-Sn phase with higher laser power, resulting in a larger eutectic network area fraction. In contrast, MR produces solder joints with minimal voids and a thicker intermetallic compound (IMC) layer. LAB-formed joints exhibit higher high-speed shear strength and lower brittle fracture rates compared to MR. The key factor in the reduced brittle fracture in LAB joints is the thinner IMC layer at the joint interface. This study highlights the potential of LAB in enhancing the mechanical reliability of solder joints in advanced electronic packaging applications. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |