Dissolution of Nb(C,N) During Post-weld Heat-Treatment of Electric Resistance Welded X70 Line Pipe. |
المؤلفون: |
Li, Leijun, Ravikiran, Kopparthi, Sharma, Nitin Kumar, Choudhury, Suvan Dev, Kannan, Rangasayee, Gaudet, Michael J., Anderson, Neil |
المصدر: |
Metallurgical & Materials Transactions. Part A; Sep2024, Vol. 55 Issue 9, p3351-3363, 13p |
مصطلحات موضوعية: |
ELECTRON energy loss spectroscopy, ELECTRIC welding, RESISTANCE welding, ELECTRIC resistance, HEAT treatment |
مستخلص: |
The effect of peak temperature for post-weld heat treatment (PWHT) on the dissolution of Nb-rich carbonitrides, Nb(C,N), in the weldline of an electric resistance welded (ERW) X70 grade pipeline steel was investigated. Selected-area electron diffraction patterns and corresponding electron energy loss spectroscopy mappings revealed both Nb-rich carbonitrides and Ti-rich nitrides, (Ti,Nb)N, in the sample heat-treated to 1080 °C peak temperature. However, only Ti-rich nitrides were revealed in the sample heat-treated to 1220 °C peak temperature. During continuous heating to higher than the Ac3 temperature, i.e., near 1100 °C temperature, the dissolution of Nb(C,N) was observed in dilation and derivative of dilation. This experimental result agreed with the predictions by a DICTRA model. Furthermore, a phenomenological model was developed to explain the volume shrinkage during the dissolution of Nb(C,N) precipitates. [ABSTRACT FROM AUTHOR] |
|
Copyright of Metallurgical & Materials Transactions. Part A is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |