Influence of Y2O3 and Cr2O3 on Formation of Microstructure and Properties as well as Accuracy of Reproduction of Geometric Characteristics during 3D Printing with Ceramics Based on Al2O3–ZrO2 |
| المؤلفون: |
Kotelnikov, N. L., Goldberg, M. A., Obolkina, T. O., Smirnov, S. V., Antonova, O. S., Barinov, S. M., Komlev, V. S. |
| المصدر: |
Inorganic Materials: Applied Research; Aug2024, Vol. 15 Issue 4, p1031-1038, 8p |
| مستخلص: |
Abstract—Powders and ceramic composite materials in an Al2O3–ZrO2 system with a concentration of ZrO2 of 20 wt % are obtained. The effect of introduction of chromium oxide and yttrium oxide into Al2O3–ZrO2 ceramic materials on the phase composition, porosity, microstructure, and mechanical properties is studied. It is shown that the introduction of chromium oxide leads to the improvement of sintering and mechanical properties of the ceramic. Products with the predefined shape of a corresponding computer model are obtained by 3D printing, and also their multistage thermal treatment is carried out. Densely sintered ceramic materials are obtained at 1550 and 1600°C, the open porosity of which is below 1% and microhardness is up to 1646 ± 50 HV. The samples are characterized by a dense microstructure with the grain size of zirconium dioxide from 400 nm to 2 μm and of aluminum oxide from 800 nm to 3 μm. The thickness of the layer formed during 3D printing shows a positive impact of the addition of Cr2O3 on the resolution during 3D printing. [ABSTRACT FROM AUTHOR] |
|
Copyright of Inorganic Materials: Applied Research is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |