Depth profiles of electron and hole traps generated by reactive ion etching near the surface of 4H-SiC. |
| المؤلفون: |
Kozakai, Shota, Fujii, Haruki, Kaneko, Mitsuaki, Kimoto, Tsunenobu |
| المصدر: |
Journal of Applied Physics; 9/7/2024, Vol. 136 Issue 9, p1-11, 11p |
| مصطلحات موضوعية: |
SCHOTTKY barrier diodes, DEPTH profiling, CONDUCTION bands, VALENCE bands, NUMERICAL calculations, ELECTRON traps |
| مستخلص: |
Deep levels in the whole bandgap of 4H-SiC generated by reactive ion etching (RIE) are investigated with both n- and p-type SiC Schottky barrier diodes by deep-level transient spectroscopy (DLTS). Depth profiles of the observed deep levels were analyzed using the DLTS peak intensities at various bias voltages and numerical calculations. The major electron traps detected after RIE and subsequent annealing at 1300 ° C include the Z 1 / 2 (E C − 0.66 eV), ON1 (E C − 0.88 eV), ON2 (E C − 0.95 eV), and EH 6 / 7 (E C − 1.50 eV) centers, and the major hole traps include the UK1 (E V + 0.51 eV), UK2 (E V + 0.72 eV), HK0 (E V + 0.77 eV), HK2 (E V + 0.79 eV), and HK3 (E V + 1.31 eV) centers, where E C and E V denote the conduction and valence band edges, respectively. Most of the traps were localized near the surface (<0.5 μ m) with a maximum density of about 1 × 10 15 cm − 3 , but several traps such as the ON1 and HK0 centers penetrate deep into the bulk region (>2 μ m). By annealing at 1400 ° C, most of the hole traps were eliminated, but several electron traps remained. From these results, the origins of these defects are discussed. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Scitation.