العنوان: |
Direct observation of amorphous to crystalline phase transitions in nanoparticle arrays of phase change materials. |
المؤلفون: |
Raoux, Simone, Rettner, Charles T., Jordan-Sweet, Jean L., Kellock, Andrew J., Topuria, Teya, Rice, Philip M., Miller, Dolores C. |
المصدر: |
Journal of Applied Physics; Nov2007, Vol. 102 Issue 9, p094305, 8p, 8 Diagrams, 1 Chart, 2 Graphs |
مصطلحات موضوعية: |
CRYSTALLIZATION, NANOPARTICLES, THICK films, SURFACES (Technology), PHASE transitions |
مستخلص: |
We have used time-resolved x-ray diffraction to study the amorphous-crystalline phase transition in 20–80 nm particles of the phase change materials Ge2Sb2Te5, nitrogen-doped Ge2Sb2Te5, Ge15Sb85, Sb2Te, and Sb2Te doped with Ag and In. We find that all samples undergo the phase transition with crystallization temperatures close to those of similarly prepared blanket films of the same materials with the exception of Sb2Te that shows the transition at a temperature that is about 40 °C higher than that of blanket films. Some of the nanoparticles show a difference in crystallographic texture compared to thick films. Large area arrays of these nanoparticles were fabricated using electron-beam lithography, keeping the sample temperatures well below the crystallization temperatures so as to produce particles that were entirely in the amorphous phase. The observation that particles with diameters as small as 20 nm can still undergo this phase transition indicates that phase change solid-state memory technology should scale to these dimensions. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |