Pendent Polyimides using Mellitic Acid Dianhydride. IV. Effect of Increased Zirconium-Pendent Group Content on Polymer Properties. |
| المؤلفون: |
Chow, Derek, Wei Cheng, Huixiong Dai, Wagner, Shawn R., Luzzi, Scott D., Landi, Brian J., Liling He, Illingsworth, Marvin L., Siochi, Emilie J. |
| المصدر: |
High Performance Polymers; Dec2009, Vol. 21 Issue 6, p744-764, 21p, 2 Diagrams, 3 Charts, 3 Graphs |
| مصطلحات موضوعية: |
POLYIMIDES, POLYMER analysis, HYDRIDES, SPECTRUM analysis, ZIRCONIUM, MOLECULAR weights, PHYSICAL & theoretical chemistry |
| مستخلص: |
For co-polyimides (PIs) of mellitic acid dianhydride, 1,3-aminophenoxybenzene and 4,4′- oxydiphthalic anhydride, Zr-pendent group content could be increased to 50% (mol) improving atomic oxygen (AO) resistance while retaining good film properties. Spectral data are consistent with expected structures. Intrinsic viscosities of 0.54-0.60 dL g-1 and average molecular weights of 111 000-122 000 gmol-1 estimated from gel permeation chromatography confirm the polymeric nature of co-polyamic acid precursors. Nuclear magnetic resonance integrations and amounts of thermogravimetric analysis residue verify pendent group concentrations. Increasing Zr-pendent group concentration from 10 to 50% (mol) caused glass transition temperatures to increase (198-245 °C), decomposition temperatures to decrease (518-455 °C), and the number of film layers able to be fabricated prior to crack formation to decrease (10 to 8). These numbers of layers were much higher than those for other PIs with comparable Zr-pendent group concentrations. Increased pendent group concentration caused the amount of protective oxide layer formed upon AO exposure to increase. [ABSTRACT FROM AUTHOR] |
|
Copyright of High Performance Polymers is the property of Sage Publications Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |