التفاصيل البيبلوغرافية
العنوان: |
Fabrication and characterization of FeRh nanoparticles. |
المؤلفون: |
Ko, Hnin Yu Yu, Suzuki, Takao, Phuoc, Nguyen N., Cao, Jiangwei |
المصدر: |
Journal of Applied Physics; Apr2008, Vol. 103 Issue 7, p07D508, 3p |
مستخلص: |
The magnetic and structural properties of FexRh100-x (x=35–80) nanoparticles fabricated by a solution phase chemical method have been studied systematically. From x-ray diffraction results, as-deposited nanoparticles of FeRh reveal a chemically disordered fcc structure which can be transformed into CsCl-type structure through thermal annealing. The high-resolution transmission electron microscopy observations of FeRh nanoparticles indicate that the average size of 3–5 nm in as-deposited state and larger size (10–15 nm) particles are also distributed in the annealed sate. Nanoparticles with x=35–55 exhibit the behaviors of magnetization with temperature, which suggests the transition from the AFM to FM phases at around 100–200 °C, whereas those with x=80 do very little change of magnetization with temperature. It is also found that there seems an effect of applied magnetic field on transition, that is, the transition temperature is shifted to a lower side upon the application of magnetic field during the transition process. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |