| العنوان: |
New-generation curing units and short irradiation time: The degree of conversion of microhybrid composite resin. |
| المؤلفون: |
Scotti, Nicola, Venturello, Alberto, Migliaretti, Giuseppe, Pera, Francesco, Pasqualini, Damiano, Geobaldo, Francesco, Berutti, Elio |
| المصدر: |
Quintessence International; 2011, Vol. 42 Issue 8, pe89-e95, 7p, 3 Charts, 1 Graph |
| مصطلحات موضوعية: |
ANALYSIS of variance, BIOPHYSICS, COMPARATIVE studies, DENTAL resins, MATERIALS testing, RESEARCH methodology, STATISTICS, TIME, STATISTICAL significance, REPEATED measures design, DATA analysis software |
| مستخلص: |
This in vitro study investigated the depth of cure of a microhybrid composite resin when cured with reduced times of exposure to three commercially available curing lights. Different sample thicknesses (1, 2, and 3 mm) were light cured in high intensity polymerization mode (2,400 mW/cm2 for 5, 10, 15, and 20 seconds; 1,100 mW/cm2 for 10, 20, 30, and 40 seconds; and 1,100 mW/cm2 for 10, 20, 30, and 40 seconds, respectively). The degree of conversion (%) at the bottom of each sample was measured by Attenuated Total Reflection Fourier Transform Infrared (ATR F-TIR) analysis after each polymerization step. Data were analyzed by ANOVA for repeated measures, showing the degree of conversion was not influenced by the curing light employed (P = .622) but was significantly influenced by the thickness of composite resin (P < .05). Variations in the degree of conversion vs the shorter irradiation time permitted (T1) were not significant among different lamps but were significant among different thicknesses. The depth of cure of microhybrid composite resin appears not to be influenced by the curing light employed. Increased irradiation time significantly increases the degree of conversion. Thickness strongly influences depth of cure. (Quintessence Int 2011;42:e89-e95) [ABSTRACT FROM AUTHOR] |
|
Copyright of Quintessence International is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |