The study of negative thermal expansion and magnetic evolution in antiperovskite compounds Cu0.8-xSnxMn0.2NMn3(0 ≤ x ≤ 0.3). |
| المؤلفون: |
Lin, J. C., Wang, B. S., Lin, S., Tong, P., Lu, W. J., Zhang, L., Song, W. H., Sun, Y. P. |
| المصدر: |
Journal of Applied Physics; Feb2012, Vol. 111 Issue 4, p043905, 6p, 7 Graphs |
| مصطلحات موضوعية: |
TIN research, LATTICE dynamics, ANTIFERROMAGNETISM, MAGNETIZATION, THERMAL expansion |
| مستخلص: |
With increasing the substitution of Sn for Cu in Cu0.8-xSnxMn0.2NMn3, the initial cubic-tetragonal structural phase transition disappears for the samples x ≥ 0.10 and is replaced by a discontinuous lattice expansion with a cubic structure which has been confirmed by the measurements of variable temperature x-ray diffractions and specific heat. The discontinuous lattice expansion broadens with increasing the doping level x and the negative thermal expansion coefficient up to -64.54 ppm/K between 190 K and 235 K is found for the sample x = 0.3. Detailed magnetic measurements indicate that the magnetic ground state is meta-stable for the lower-doping level and transforms into spin-glass-like state owing to the enhancement of antiferromagnetic interaction when x is up to 0.3. Furthermore, the magnetization curves M(T) display abnormal behaviors for lower-x. For the samples x = 0.1 and 0.2, the jump of field-cooled magnetization curve MFC (defined as ΔMFC/MFC) around the lower-temperature magnetic transition is suppressed with increasing the magnetic field. These abnormalities of magnetizations are also discussed based on a simple model. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Scitation.