Magnetic and structural characterization and ferromagnetic resonance study of thin film HITPERM soft magnetic materials for data storage applications. |
| المؤلفون: |
Okumura, H., Twisselmann, D. J., McMichael, R. D., Huang, M. Q., Hsu, Y. N., Laughlin, D. E., McHenry, M. E. |
| المصدر: |
Journal of Applied Physics; 5/15/2003, Vol. 93 Issue 10, p6528, 3p, 1 Black and White Photograph, 1 Chart, 2 Graphs |
| مصطلحات موضوعية: |
THIN films, IRON compounds, AMORPHOUS substances, INFORMATION retrieval |
| مستخلص: |
HITPERM/SiO[SUB2] single and multilayer thin films have been produced using a target composition of Fe[SUB]70Co[SUB30])[SUB88]Zr[SUB7]B[SUB4]Cu[SUB1]. The as-deposited HITPERM film contains small bcc (or B2) nanocrystals of volume fraction less than 10% surrounded by an amorphous matrix. The lattice parameter of the nanocrystal is about 5% larger than an equilibrium FeCo phase. The saturation induction determined from FMR measurements (1.53±0.08 T) is consistent with VSM and SQUID measurements (1.45-1.5 T) and also with as-spun amorphous ribbons (1.55-1.62 T). The Landé g-factors (2.15±0.05) are typical of transition metals, particularly, of Fe. The Landau-Lifshitz-Gilbert damping parameters of the single and multilayered films are small (α=5 0.005±60.0004) with each layer acting almost independently. Neither thickness variation of each layer nor the number of stacking significantly affects the damping process in a range of film thicknesses of 50-150 nm, while the coercivities are strongly dependent on those parameters. This supports a notion that the damping parameter is an intrinsic property. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |