| العنوان: |
Determination of the fixed oxide charge and interface trap densities for buried oxide layers formed by oxygen implantation. |
| المؤلفون: |
Brady, F. T., Li, S. S., Burk, D. E., Krull, W. A. |
| المصدر: |
Applied Physics Letters; 3/14/1988, Vol. 52 Issue 11, p886, 3p |
| مصطلحات موضوعية: |
OXIDES, METAL oxide semiconductors |
| مستخلص: |
Capacitance-voltage measurements were used to analyze buried oxide layers formed by the implantation of oxygen into silicon substrates. The analysis is based on the extension of conventional metal/oxide/semiconductor capacitor theory to the two buried oxide interfaces of the epilayer/oxide/substrate structure. The processing parameters include oxygen doses of 1.8 or 2.0×1018 cm-2, implant temperature of 500 °C, and anneal temperature of 1250 °C for 2 or 16 h. The results are fixed oxide charge densities of 2–3×1011 and 1–2×1010 cm-2 for the epi/oxide and substrate/oxide interfaces, respectively; interface trap densities are 0.5 to 2×1011 cm-2 eV-1 for the epi/oxide interface, and not measurable for the substrate/oxide interface. The epilayer/oxide interface was found to be more sensitive to processing variations than the substrate/oxide interface. [ABSTRACT FROM AUTHOR] |
|
Copyright of Applied Physics Letters is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |