التفاصيل البيبلوغرافية
العنوان: |
Electrical Conductivity, Liquidus Temperatures and Raman Spectra of YbCl3-KCl-Yb2O3 and YbCl3-KCl-NaCl-Yb2O3 Systems. |
المؤلفون: |
Nikolaeva, Elena V., Zakiryanova, Irina D., Bovet, Andrey L., Korzun, Iraida V. |
المصدر: |
Journal of The Electrochemical Society; Jan2021, Vol. 168 Issue 1, p1-8, 8p |
مصطلحات موضوعية: |
LIQUIDUS temperature, RAMAN spectroscopy, ELECTRIC conductivity, ELECTRICAL conductivity measurement, YTTERBIUM |
مستخلص: |
The electrical conductivity of 0.507KCl-0.493YbCl3 and 0.5YbCl3-0.25KCl-0.25NaCl chloride melts with the ytterbium oxide (Yb2O3) additions ranging from 0 to 3.15 mol% was measured depending on both the temperature and concentration of Yb2O3. The liquidus temperatures of the studied systems containing from 0 to 3.35 mol.% Yb2O3 were determined by DSC method and the electrical conductivity measurements. The Yb2O3 additions increase the liquidus temperatures of the systems under study. The high-temperature Raman spectra of chloride (YbCl3-KCl-NaCl) and oxide-chloride (YbCl3-KCl-NaCl-Yb2O3) melts were recorded. In the oxide-chloride melt an additional band was detected in the region of 460 cm-1 corresponding to stretchingvibrations of the Yb-O bond in [OYb3Cln] oxychloride associates. There was no evidence of vibrational bands related to ytterbium oxide. Such changes in the Raman spectrum points to the dissociation of ytterbium oxide and modifications to the local structure of the chloride melt. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of The Electrochemical Society is the property of IOP Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |