Fracture strength and bonding interface morphology of CAD/CAM-fabricated ceramic laminate veneers on bleached enamel treated with two different antioxidants. |
| المؤلفون: |
Hong ZHANG, Jiawen CHEN, Ying WANG, Yiyan YU, Yuanhang ZHAO, Jiazhuo SONG, Zhimin ZHANG |
| المصدر: |
Dental Materials Journal; 2023, Vol. 42 Issue 4, p559-567, 9p |
| مصطلحات موضوعية: |
FRACTURE strength, BOND strengths, LAMINATED materials, VITAMIN C, ENAMEL & enameling |
| مستخلص: |
This study aimed to investigate the effects of two antioxidants and their application time on the fracture strength of computer-aided design and computer-aided manufacturing (CAD/CAM)-fabricated ceramic laminate veneers to bleached enamel, as well as their effects on the bonding interface micromorphology. Eight groups were set: Group NC (without bleaching and antioxidant treatment); Group NA (bleaching without antioxidant treatment); Group SA30, SA60, SA120 and Group PAC30, PAC60, PAC120 (bleaching and treating with sodium ascorbate or proanthocyanidins for 30, 60, and 120 min, respectively). After cementation of veneers, fracture strength values and failure modes were analyzed. The bonding interface morphology was observed by confocal laser scanning microscopy. The fracture strength was impaired when cementation procedure was performed immediately after bleaching. This reduction in fracture strength was reestablished with antioxidant treatment, and an extended treatment time contributed to better improvement. The resin tags at the bonding interfaces of the bleached enamel were impaired. Antioxidant treatments were able to reverse this unfavorable trend. [ABSTRACT FROM AUTHOR] |
|
Copyright of Dental Materials Journal is the property of Japanese Society for Dental Materials & Devices and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Supplemental Index |