"In vitro" surface roughness of different glass ionomer cements indicated for ART restorations. |
| المؤلفون: |
Momesso, Marília Gabriela Corrêa, da Silva, Renata Cristiane, Imparato, José Carlos Pettorossi, Molina, Celso, Navarro, Ricardo Scarparo, Ribeiro, Sidney José Lima |
| المصدر: |
Brazilian Journal of Oral Sciences; 2010, Vol. 9 Issue 2, p77-80, 4p, 3 Black and White Photographs, 1 Chart |
| مصطلحات موضوعية: |
SURFACE roughness, IONOMERS, ADHESIVE cements, SUBSTRATES (Materials science), ANALYSIS of variance, PARTICLE size determination |
| مستخلص: |
Aim: The aim of this in vitro study was to evaluate the surface roughness of three glass ionomer cements (GICs) indicated for ART restorations. Methods: Ten cylindrical specimens of three commercial glass ionomers cements (Vidrion R - S.S. White, Maxxion R - FGM and Vitromolar DFL) were prepared (n=30) without surface finishing or protection. Twenty-four hours after preparation, the surface roughness measurements were obtained as the mean of three readings of the surface of each specimen by profilometry. The roughness values (Ra, μm) were subjected to one-way ANOVA and Tukey's test (p<0.05). Results: No statistically significant differences were observed between Vidrion R (0.18 ± 0.05) and Vitromolar (0.21 ± 0.05), whereas Maxxion R presented significantly higher roughness values than those of the other materials. Conclusions: It may be concluded that characteristics of particle size and composition of the different GICs affected their surface roughness 24 h after preparation. [ABSTRACT FROM AUTHOR] |
|
Copyright of Brazilian Journal of Oral Sciences is the property of Brazilian Journal of Oral Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |