Effect of Lubrication Conditions on the Forming Limit of Deep Drawing of 6061 Aluminum Alloy Sheet
| العنوان: | Effect of Lubrication Conditions on the Forming Limit of Deep Drawing of 6061 Aluminum Alloy Sheet |
|---|---|
| المؤلفون: | Wang, Yan Qi, Cheng, Yong Qi, Zhang, Peng, Luo, Gan, Li, Peng Bin, Jiang, Kui |
| المصدر: | Materials Science Forum; January 2019, Vol. 944 Issue: 1 p85-91, 7p |
| مستخلص: | With the development of lightweight vehicles, aluminum alloy sheets are increasingly used in the automotive field. However, the aluminum alloy sheet has poor forming performance at room temperature. Therefore, how to improve the sheet metal forming performance of aluminum alloy sheet has become one of the current research hotspots. In this paper, the effects of different lubricants on the deep drawing forming properties of 6061 aluminum alloy sheets were studied by cupping experiments. The effects of lubricants on the deep drawing of sheet metal forming and the wall thickness of cups after deep drawing were explored. The results show that under the condition of drawing speed of 3MPa and 200mm/min, the ultimate drawing ratio of the sheet under oil lubrication is 1.92, and the PTFE film is 2.16. Grease and graphite lubrication are respectively 2.12 and 2.03, using PTFE film lubrication can increase by about 10% contrast with the oil lubrication. The measurement of the wall thickness of the cup under the forming limit state shows that the position with the largest reduction rate appears in the rounded transition zone, and the wall portion of the cylindrical member increases with the height of the wall, and the thickness from the bottom of the cup to the bottom of the cup. The edges all show a trend of decreasing first and then increasing. |
| قاعدة البيانات: | Supplemental Index |
Full Text Finder | تدمد: | 02555476 16629752 |
|---|---|
| DOI: | 10.4028/www.scientific.net/MSF.944.85 |