Investigation of the use of nano-titanium dioxide particles synthesized by reflux method as a whitener agent in standard porcelain tiles
| العنوان: | Investigation of the use of nano-titanium dioxide particles synthesized by reflux method as a whitener agent in standard porcelain tiles |
|---|---|
| المؤلفون: | Tamsu Selli, N., Basaran, N., Kesmez, Ö. |
| المصدر: | Boletín de la Sociedad Española de Cerámica y Vidrio; 20230101, Issue: Preprints |
| مستخلص: | The effects of adding zircon and synthesized TiO2nanoparticles (NPs) to standard porcelain tiles on mechanical and optical properties were studied. The obtained TiO2nanoparticles had an average particle size of 7.47 nm. The optical properties of TiO2NPs were characterized by using UV-visible spectrophotometer. The synthesized TiO2NPs and commercial zircon were added to standard porcelain tile composition at a rate of 1%, 2% and 4% by weight. Phase analyzes of the samples were made with XRD, and microstructure analyzes were made with SEM/EDS. Optical dilatometer test was used for sintering studies and densification behavior was observed with water absorption test. The optical behaviour of the samples was analysed using spectrophotometric measurements (CIELab method). As a result of this test, it was observed that nano-sized titanium oxide can be used as a whitening agent in porcelain tiles. In addition, the additives made to porcelain tiles also contributed to the increase in mechanical properties. |
| قاعدة البيانات: | Supplemental Index |
Full Text Finder | تدمد: | 03663175 21730431 |
|---|---|
| DOI: | 10.1016/j.bsecv.2023.05.001 |