(3 + 1)-Dimensional commensurately modulated structure and photoluminescence properties of diborate KSbOB2O5
العنوان: | (3 + 1)-Dimensional commensurately modulated structure and photoluminescence properties of diborate KSbOB2O5 |
---|---|
المؤلفون: | Yun-Chang Fan, Fei-Fei Li, Dan Zhao, Bing-Guo Liu, Rong-Hua Zhang, Juan Yang |
المصدر: | Dalton Transactions. 44:6277-6287 |
بيانات النشر: | Royal Society of Chemistry (RSC), 2015. |
سنة النشر: | 2015 |
مصطلحات موضوعية: | Inorganic Chemistry, Diffraction, Crystallography, Formalism (philosophy of mathematics), Photoluminescence, Materials science, One-dimensional space, Orthorhombic crystal system, Superspace, Single crystal |
الوصف: | Single-crystal diborate KSbOB2O5 has been prepared under a high temperature molten-salt method and its structure has been determined by single crystal X-ray diffraction analysis. The diffraction pattern shows strong main reflections and weak satellite reflections, clearly indicating a modulated structure. Using the four-dimensional superspace formalism for aperiodic structures, its reflections could be indexed as orthorhombic superspace group Pmn21(0β0)s00 with the modulation vector q = 5/12b*, and then the structure solution and refinement reached a final commensurately modulated model that was refined extremely well and did not show any unusual features. On the other hand, the powder sample of KSbOB2O5 was synthesized by the high-temperature solid-state reaction method, and the powder X-ray diffraction pattern fits very well with the simulated from the single-crystal data. In addition, photoluminescence properties of diborate KSbOB2O5 activated by 4.5 mol% Dy3+ have been studied, indicating an extraordinary phenomenon that the red emission at around 635 nm (4F9/2 → 6H11/2) is much stronger than the yellow emission at around 581 nm (4F9/2 → 6H13/2). |
تدمد: | 1477-9234 1477-9226 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::039afe4fe2ed0d3da2a09cae1e8a1972 https://doi.org/10.1039/c5dt00267b |
رقم الأكسشن: | edsair.doi...........039afe4fe2ed0d3da2a09cae1e8a1972 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 14779234 14779226 |
---|