Transparent Conductive ITO/Ag/ITO Electrode Deposited at Room Temperature for Organic Solar Cells
العنوان: | Transparent Conductive ITO/Ag/ITO Electrode Deposited at Room Temperature for Organic Solar Cells |
---|---|
المؤلفون: | Hyeong Seop Im, Seok-In Na, Jun Ho Kim, Tae Woon Kang, Sung-Nam Kwon, Tae Yeon Seong, Young Zo Yoo |
المصدر: | Journal of Electronic Materials. 46:306-311 |
بيانات النشر: | Springer Science and Business Media LLC, 2016. |
سنة النشر: | 2016 |
مصطلحات موضوعية: | 010302 applied physics, Materials science, Organic solar cell, business.industry, Energy conversion efficiency, 02 engineering and technology, Surface finish, 021001 nanoscience & nanotechnology, Condensed Matter Physics, 01 natural sciences, Polymer solar cell, Electronic, Optical and Magnetic Materials, Anode, Root mean square, Optics, 0103 physical sciences, Electrode, Materials Chemistry, Transmittance, Optoelectronics, Electrical and Electronic Engineering, 0210 nano-technology, business |
الوصف: | We investigated the optical and electrical properties of room-temperature-deposited indium-tin-oxide (ITO)/Ag (19 nm)/ITO multilayer films as a function of ITO layer thickness. The optical and electrical properties of the ITO/Ag/ITO films were compared with those of high-temperature-deposited ITO-only films for use as an anode in organic solar cells (OSCs). The ITO/Ag/ITO multilayer films had sheet resistances in the range 5.40–5.78 Ω/sq, while the ITO-only film showed 14.18 Ω/sq. The carrier concentration of the ITO/Ag/ITO films gradually decreased from 2.01 × 1022 to 7.20 × 1021 cm−3 as the ITO thickness increased from 17 nm to 83 nm. At 530 nm, the transmittance of the ITO/Ag/ITO (50 nm/19 nm/50 nm) films was ~90%, while that of the ITO-only film gave 96.5%. The multilayer film had a smooth surface with a root mean square (RMS) roughness of 0.49 nm. Poly (3-hexylthiophene) (P3HT):[6,6]-phenyl-C61 butyric acid methylester (PCBM) bulk heterojunction (BHJ)-based OSCs fabricated with the ITO/Ag/ITO (50 nm/19 nm/50 nm) film showed a power conversion efficiency (PCE) (2.84%) comparable to that of OSCs with a conventional ITO-only anode (3.48%). |
تدمد: | 1543-186X 0361-5235 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::35fce33d6dd7e4e5397d3eb9e524db1f https://doi.org/10.1007/s11664-016-4956-9 |
حقوق: | CLOSED |
رقم الأكسشن: | edsair.doi...........35fce33d6dd7e4e5397d3eb9e524db1f |
قاعدة البيانات: | OpenAIRE |
تدمد: | 1543186X 03615235 |
---|