Elastic modulus of shape-memory NiTi fromin situneutron diffraction during macroscopic loading, instrumented indentation, and extensometry
العنوان: | Elastic modulus of shape-memory NiTi fromin situneutron diffraction during macroscopic loading, instrumented indentation, and extensometry |
---|---|
المؤلفون: | Sudhir Rajagopalan, A. L. Little, Mark A.M. Bourke, Raj Vaidyanathan |
المصدر: | Applied Physics Letters. 86:081901 |
بيانات النشر: | AIP Publishing, 2005. |
سنة النشر: | 2005 |
مصطلحات موضوعية: | Materials science, Physics and Astronomy (miscellaneous), Neutron diffraction, Modulus, Young's modulus, Poisson's ratio, Condensed Matter::Materials Science, symbols.namesake, Crystallography, Indentation, Lattice plane, symbols, Composite material, Crystal twinning, Elastic modulus |
الوصف: | The elastic modulus of B19’ shape-memory NiTi was determined using three techniques; from the response of lattice planes measured using in situ neutron diffraction during loading, instrumented indentation using a spherical indenter and macroscopic extensometry. The macroscopic measurements resulted in a modulus of 68 GPa, significantly less than the 101 GPa from indentation and the lattice plane average of 109 GPa from neutron diffraction. Evidence from the neutron measurements suggests that the disparity derives from the onset of small amounts of twinning at stresses less that 40 MPa, which might otherwise be considered elastic from a macroscopic view point. |
تدمد: | 1077-3118 0003-6951 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::4cf7d2e51bc92bd01b6fd1351b6ba5c3 https://doi.org/10.1063/1.1863437 |
رقم الأكسشن: | edsair.doi...........4cf7d2e51bc92bd01b6fd1351b6ba5c3 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 10773118 00036951 |
---|