Dislocation densities of dispersion-strengthened copper with aluminum oxide, namely GlidCop were evaluated employing the X-ray line profile analysis using the modified Williamson-Hall and modified Warren-Averbach method. X-ray diffraction profiles for GldCop samples with compressive strains applied at ambient temperature were measured with synchrotron radiation. The dislocation densities of GlidCop with compressive strain ranging from 0 – 2.7 % were on the order of 1.5×1014 – 6.6×1014 m-2.