Fabricating 43-μm-Thick and 12% Efficient Heterojunction Silicon Solar Cells by Using Kerfless Si(111) Substrates
| العنوان: | Fabricating 43-μm-Thick and 12% Efficient Heterojunction Silicon Solar Cells by Using Kerfless Si(111) Substrates |
|---|---|
| المؤلفون: | Teng Yu Wang, Peichen Yu, Chien Hsun Chen, J. Andrew Yeh, Chun Ming Yeh, Chun Heng Chen, Chen-Hsun Du, Jui Chung Hsiao |
| المصدر: | ECS Journal of Solid State Science and Technology. 4:P319-P323 |
| بيانات النشر: | The Electrochemical Society, 2015. |
| سنة النشر: | 2015 |
| مصطلحات موضوعية: | Materials science, Silicon, business.industry, chemistry.chemical_element, Heterojunction, Substrate (electronics), Surface finish, Electronic, Optical and Magnetic Materials, Metal, Reflection (mathematics), chemistry, Etching (microfabrication), visual_art, visual_art.visual_art_medium, Optoelectronics, business, Layer (electronics) |
| الوصف: | A 43-μm-thick Si(111) substrate was obtained using the stress-induced lift-off method with a screen-printed metal paste layer as the stress-generation layer. The reflection of the metal-removed side of the Si(111) substrate was lower than that of the exfoliated side because of high surface roughness resulting from the reaction between the metal paste and the silicon substrate at 700◦C. After aggressive etching with an alkaline solution for the peeled silicon substrate, the efficiency of the heterojunction silicon solar cell was improved from 0.87% to 12%. © The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY, http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited. [DOI: 10.1149/2.0171508jss] All rights reserved. |
| تدمد: | 2162-8777 2162-8769 |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::a8527e01e78ff569988eed8d42d4fe9e https://doi.org/10.1149/2.0171508jss |
| رقم الأكسشن: | edsair.doi...........a8527e01e78ff569988eed8d42d4fe9e |
| قاعدة البيانات: | OpenAIRE |
| تدمد: | 21628777 21628769 |
|---|