Low-temperature deposited polycrystalline silicon waveguides are emerging as a flexible platform that allows for dense optoelectronic integration. Here, the optical transmission properties of poly-silicon waveguides have been characterized from the near-to-mid-infrared wavelength regime, extending the optical transmission well beyond previous reports in the telecom band. The poly-Si waveguides with a dimension of 3 µm × ∼0.6 µm have been produced from pre-patterned amorphous silicon waveguides that are post-processed through laser melting, reflowing, and crystallization using a highly localized laser induced heat treatment at a wavelength of 532 nm. Low optical transmission losses (−1) have been observed at 1.55 µm as well as across the wavelength range of 2−2.25 µm, aided by the relatively large waveguide heights that are enabled by the deposition process. The results demonstrate the suitability of low-temperature poly-silicon waveguides to find wide ranging applications within integrated mid-infrared systems.