Asymmetric bismaleimide-based high-performance resins with improved processability and high Tg over 400 °C
العنوان: | Asymmetric bismaleimide-based high-performance resins with improved processability and high Tg over 400 °C |
---|---|
المؤلفون: | Ren Zhidong, Si-Jia Hao, Dai Shenglong, Yang Cheng, Xing Yue |
المصدر: | High Performance Polymers. 31:1132-1139 |
بيانات النشر: | SAGE Publications, 2019. |
سنة النشر: | 2019 |
مصطلحات موضوعية: | Matrix (mathematics), Materials science, Polymers and Plastics, Chemical engineering, Organic Chemistry, Materials Chemistry |
الوصف: | Asymmetric 2-(4′-maleimido)phenyl-2-(4′-maleimidophenoxyl)phenylbutane (EBA-BMI) was successfully mixed with N, N′-(4,4′-diphenylmethane)bismaleimide (DDM-BMI) to prepare the matrix resins for high-temperature fiber-reinforced polymeric composites (glass transition temperature ( Tg) > 400°C). Experimental results imply that DDM-BMI/EBA-BMI (DE-BMIs) show excellent melting performance with wide processing temperature window and low molten viscosity, suggesting excellent compatibility between DDM-BMI and EBA-BMI. For example, the viscosity of DE-BMI41 (DDM-BMI/EBA-BMI, 4/1) is about 474–51 mPa·s in the temperature range of 148–180 °C. In addition, cured DE-BMIs represent remarkable thermal properties with Tg over 400°C, under which the storage modulus could still reach as high as 3.2 GPa. Meanwhile, the coefficient of thermal expansion of these cured resins is about 36–40 ppm °C−1 at 50–250°C, and the 5% weight loss temperature is about 470°C. |
تدمد: | 1361-6412 0954-0083 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::f1bef1e74807fb6edce3f686896d9901 https://doi.org/10.1177/0954008319826368 |
حقوق: | CLOSED |
رقم الأكسشن: | edsair.doi...........f1bef1e74807fb6edce3f686896d9901 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 13616412 09540083 |
---|