Microstructural Analysis of Superconducting Joint Fabricated Using CJMB Between Gd123-Coated Conductors
العنوان: | Microstructural Analysis of Superconducting Joint Fabricated Using CJMB Between Gd123-Coated Conductors |
---|---|
المؤلفون: | Yasuteru Mawatari, Shinji Hirai, Yoshinori Tayu, Toshihiro Kuzuya, Xinzhe Jin, Yoshinori Yanagisawa, Y. Amakai, Naoki Momono |
المصدر: | IEEE Transactions on Applied Superconductivity. 29:1-5 |
بيانات النشر: | Institute of Electrical and Electronics Engineers (IEEE), 2019. |
سنة النشر: | 2019 |
مصطلحات موضوعية: | Diffraction, Superconductivity, coated conductor, Yb123, Materials science, Joint interface, Scanning electron microscope, Gd123, Crystal growth, Condensed Matter Physics, 01 natural sciences, Electronic, Optical and Magnetic Materials, 0103 physical sciences, Ultimate tensile strength, Melting point, Electrical and Electronic Engineering, Composite material, 010306 general physics, Joint (geology), Electrical conductor |
الوصف: | A superconducting joint between two Gd123-coated conductors was successfully formed using crystal growth in the bulk (CJMB). An intermediate Yb123 layer was used at the junction, and was melted to form a joint by heat treatment at a temperature below the melting point of the RE123 (such as Gd123) in the coated conductor. This liquid-phase bonding results in high tensile strength, which has exceeded 100 MPa in previous studies. Nevertheless, the joint principle has not been sufficiently clarified. In this study, we performed microstructural analysis of the joint using X-ray diffraction and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy to form a clearer understanding of the joint formation mechanism in order to achieve a high critical current in the junction. |
وصف الملف: | application/pdf |
تدمد: | 2378-7074 1051-8223 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::0694d77eb7cdbef4e4e3a9129b9bd832 https://doi.org/10.1109/tasc.2019.2909203 |
حقوق: | OPEN |
رقم الأكسشن: | edsair.doi.dedup.....0694d77eb7cdbef4e4e3a9129b9bd832 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 23787074 10518223 |
---|