العنوان: | Structure and Electrical Properties of Na0.5Bi0.5TiO3 Epitaxial Films with (110) Orientation |
---|---|
المؤلفون: | Baoting Liu, Jie Gao, Jianmin Song, Xiuhong Dai, Laihui Luo, Suwei Zhang, Lei Zhao |
المصدر: | Crystals, Vol 9, Iss 11, p 558 (2019) Crystals Volume 9 Issue 11 |
بيانات النشر: | MDPI AG, 2019. |
سنة النشر: | 2019 |
مصطلحات موضوعية: | nbt epitaxial film, Materials science, General Chemical Engineering, ultraviolet light, 02 engineering and technology, Substrate (electronics), Epitaxy, 01 natural sciences, ferroelectric properties, law.invention, Inorganic Chemistry, law, Electric field, 0103 physical sciences, lcsh:QD901-999, Ultraviolet light, General Materials Science, Polarization (electrochemistry), 010302 applied physics, business.industry, 021001 nanoscience & nanotechnology, Condensed Matter Physics, Thermal conduction, Ferroelectricity, Capacitor, Optoelectronics, lcsh:Crystallography, 0210 nano-technology, business |
الوصف: | Pt/Na0.5Bi0.5TiO3/La0.5Sr0.5CoO3 (Pt/NBT/LSCO) ferroelectric capacitors were fabricated on (110) SrTiO3 substrate. Both NBT and LSCO films were epitaxially grown on the (110) SrTiO3 substrate. It was found that the leakage current density of the Pt/NBT/LSCO capacitor is favorable to ohmic conduction behavior when the applied electric fields are lower than 60 kV/cm, and bulk-limited space charge-limited conduction takes place when the applied electric fields are higher than 60 kV/cm. The Pt/NBT/LSCO capacitor possesses good fatigue resistance and retention, as well as ferroelectric properties with Pr = 35 &mu C/cm2. The ferroelectric properties of the Pt/NBT/LSCO capacitor can be modulated by ultraviolet light. The effective polarization, &Delta P, was reduced and the maximum polarization Pmax was increased for the Pt/NBT/LSCO capacitor when under ultraviolet light, which can be attributed to the increased leakage current density and non-reversible polarization P^ caused by the photo-generated carriers. |
وصف الملف: | application/pdf |
تدمد: | 2073-4352 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::4bfa27495c82914a9538aaaa1cc8587c https://doi.org/10.3390/cryst9110558 |
حقوق: | OPEN |
رقم الأكسشن: | edsair.doi.dedup.....4bfa27495c82914a9538aaaa1cc8587c |
قاعدة البيانات: | OpenAIRE |
تدمد: | 20734352 |
---|