Solubility of CO2 in molten Li2Co3-LiCl
| العنوان: | Solubility of CO2 in molten Li2Co3-LiCl |
|---|---|
| المؤلفون: | Z.-W. Wang, Xianwei Hu, Zhongning Shi, Jiangyu Yu, Aimin Liu, W.-T. Deng |
| المصدر: | Journal of Mining and Metallurgy. Section B: Metallurgy, Vol 57, Iss 2, Pp 279-284 (2021) |
| بيانات النشر: | Technical Faculty, Bor, 2021. |
| سنة النشر: | 2021 |
| مصطلحات موضوعية: | Exothermic reaction, Mining engineering. Metallurgy, Chemistry, solution enthalpy change, pressure differential method, Enthalpy, Metals and Alloys, TN1-997, Thermodynamics, Pressure differential, li2co3-licl melts, Geotechnical Engineering and Engineering Geology, Mechanics of Materials, Materials Chemistry, co2 solubility, Composition (visual arts), mscc-et, Solubility |
| الوصف: | Solubility of CO2 in molten Li2CO3-LiCl was measured by a pressure differential method, and the enthalpy change of the solution was calculated on that basis. The relationships between the solubility and the enthalpy change, and the temperature and the composition of the melts were discussed. The results showed that when the temperature was 873?923 K and the Li2CO3 content was 10?50 mol%, the solubility of CO2 increased with decreasing temperature and/or increasing Li2CO3 content. The maximum solubility was 3.965 ? 10?7gCO2/gmelt at 873 K when the content of Li2CO3 was 50 mol%. The solution of CO2 was exothermic. With increasing temperature and Li2CO3 content, more enthalpy was needed for CO2 solution. |
| اللغة: | English |
| تدمد: | 2217-7175 1450-5339 |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::6812c2e96813aa3d179c2a66347ed52f http://www.doiserbia.nb.rs/img/doi/1450-5339/2021/1450-53392100024H.pdf |
| حقوق: | OPEN |
| رقم الأكسشن: | edsair.doi.dedup.....6812c2e96813aa3d179c2a66347ed52f |
| قاعدة البيانات: | OpenAIRE |
| تدمد: | 22177175 14505339 |
|---|