Potassium L-ascorbate monohydrate: a new metal–organic nonlinear optical crystal
العنوان: | Potassium L-ascorbate monohydrate: a new metal–organic nonlinear optical crystal |
---|---|
المؤلفون: | K Raghavendra Rao, Tayur N. Guru Row, Suja Elizabeth, H. L. Bhat, Diptikanta Swain, Dhanpal Bairwa |
المصدر: | Applied Physics B. 127 |
بيانات النشر: | Springer Science and Business Media LLC, 2021. |
سنة النشر: | 2021 |
مصطلحات موضوعية: | Condensed Matter - Materials Science, Materials science, Physics and Astronomy (miscellaneous), Potassium, Energy conversion efficiency, General Engineering, Analytical chemistry, Materials Science (cond-mat.mtrl-sci), FOS: Physical sciences, General Physics and Astronomy, chemistry.chemical_element, L-Ascorbate, Nonlinear optical crystal, 01 natural sciences, 010309 optics, Metal, Crystal, Nonlinear optical, Differential scanning calorimetry, chemistry, visual_art, 0103 physical sciences, visual_art.visual_art_medium, 010306 general physics |
الوصف: | Large size single crystals of potassium L-ascorbate monohydrate (KLAM), (KC6H7O6.H2O) are grown using solution growth technique by lowering the temperature at the rate of 0.24 {\deg}C/h, where water was used as solvent. The structure of KLAM was solved by single crystal XRD. KLAM crystallizes in non-centrosymmetric, monoclinic, P21 space group with lattice parameters a = 7.030(5) {\AA}, b = 8.811(5) {\AA}, c = 7.638(5) {\AA} and \b{eta} = 114.891(5){\deg}. The crystal grows with bulky morphology in all three directions having (100), (-100), (-110), (0-1-1), (0-11), (001) and (00-1) prominent faces. TGA and DSC measurements show that KLAM is stable up to 80 {\deg}C. The crystal shows good optical transparency with a lower cut off as low as 297 nm. Second harmonic conversion efficiency measured on powder sample is 3.5 times that of potassium dihydrogen phosphate (KDP). Phase matching (PM) is observed on a plate of the KLAM. Noncollinear phase matching rings are also observed near the PM directions which help to identify the locus of PM directions. Presence of noncollinear SHG rings up to third order suggests large birefringence and nonlinear optical coefficients. Laser damage threshold value of the crystal is found to be 3.07 GW/cm2, at 1064 nm in 100 direction. Comment: 13 pages |
تدمد: | 1432-0649 0946-2171 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::e9803c4f547d1b66ad1e9530592084b6 https://doi.org/10.1007/s00340-020-07561-x |
حقوق: | OPEN |
رقم الأكسشن: | edsair.doi.dedup.....e9803c4f547d1b66ad1e9530592084b6 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 14320649 09462171 |
---|