Graphene Coating Obtained in a Cold-Wall CVD Process on the Co-Cr Alloy (L-605) for Medical Applications
العنوان: | Graphene Coating Obtained in a Cold-Wall CVD Process on the Co-Cr Alloy (L-605) for Medical Applications |
---|---|
المؤلفون: | Łukasz Wasyluk, Vitalii Boiko, Marta Markowska, Mariusz Hasiak, Maria Luisa Saladino, Dariusz Hreniak, Matteo Amati, Luca Gregoratti, Patrick Zeller, Dariusz Biały, Jacek Arkowski, Magdalena Wawrzyńska |
المصدر: | International Journal of Molecular Sciences, Vol 22, Iss 6, p 2917 (2021) |
بيانات النشر: | MDPI AG, 2021. |
سنة النشر: | 2021 |
المجموعة: | LCC:Biology (General) LCC:Chemistry |
مصطلحات موضوعية: | graphene coating, biocompatibility, cobalt-chromium alloy, cold-wall chemical vapor deposition method, Biology (General), QH301-705.5, Chemistry, QD1-999 |
الوصف: | Graphene coating on the cobalt-chromium alloy was optimized and successfully carried out by a cold-wall chemical vapor deposition (CW-CVD) method. A uniform layer of graphene for a large area of the Co-Cr alloy (discs of 10 mm diameter) was confirmed by Raman mapping coated area and analyzing specific G and 2D bands; in particular, the intensity ratio and the number of layers were calculated. The effect of the CW-CVD process on the microstructure and the morphology of the Co-Cr surface was investigated by scanning X-ray photoelectron microscope (SPEM), atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). Nanoindentation and scratch tests were performed to determine mechanical properties of Co-Cr disks. The results of microbiological tests indicate that the studied Co-Cr alloys covered with a graphene layer did not show a pro-coagulant effect. The obtained results confirm the possibility of using the developed coating method in medical applications, in particular in the field of cardiovascular diseases. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1422-0067 1661-6596 |
Relation: | https://www.mdpi.com/1422-0067/22/6/2917; https://doaj.org/toc/1661-6596; https://doaj.org/toc/1422-0067 |
DOI: | 10.3390/ijms22062917 |
URL الوصول: | https://doaj.org/article/045a2fc3f0fd4fc097767cec0dba95b2 |
رقم الأكسشن: | edsdoj.045a2fc3f0fd4fc097767cec0dba95b2 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 14220067 16616596 |
---|---|
DOI: | 10.3390/ijms22062917 |